1428 High performance structural bonding acrylic adhesive
Two component, blue, rigid, super fast curing methyl acrylic acid
adhesive.Suitable for plastic, metal and composite adhesive, high
viscosity, high thixotropic, not vertical flow, Mixing ratio 10:1,
Operation time 3-4 minutes, time to 75% strength: 10 minutes.
Especially suitable for bonding of composite materials, without
surface treatment can reach the highest strength, good toughness,
good shock resistance, fatigue resistance. Meet the demand of mass
Transport vehicles, notebook computer, mobile phone and other
products such as structural adhesive bonding electrons.
Bonding material: ABS, glass steel, polyester (DCPD modified)
polystyrene, polyethylene ester, PVC, polyurethane, coating
Carbon steel, aluminum and stainless steel recommended HuiTian
|Component of Basic Materials||acrylic acid|
|Mix Ratio by weight (A:B)||10:1|
|Handing Curing Time||Min||6|
|Initial Curing Time||Hour||0.5|
|Full Curing Time||Hour||24|
|Tensile Strength||After Curing||Mpa||20|
|Elongation at break||%|
|Flame Retardant Rating||UL94 V-1|
Resistance PH 3-10 acid, hydrocarbons, salt solution. Not resistant
to polar solvent, acid and alkali.
How to use
Surface treatment: Remove dust, water, oil from surface; maintain
the adhesive surface clean, carbon steel, aluminum and stainless
steel recommended Huitian primer to reach 1020 best bonding
This product at 18 ℃ -27 ℃ environment construction to achieve the
most ideal curing effect, below 18 ℃ curing slower, more than 27 ℃
curing faster. Effects of A and B components of the viscosity is
affected by temperature, in order to ensure the measurement /
consistent, effect of mixing equipment, the two components in the
storage temperature to maintain a constant.
Gluing work must finish in operation time. Operation before the end
of time, glue and positioning of the work piece to accurately
completed, then keep the work piece in a fixed state until the end
to remove positioning time.
Before curing is easier to clean, wipe the lotion, overflow
adhesive residue available containing citric acid, terpene resin or
NMP degreasing agent scrub in order to achieve the best results. If
the layer has been cured, carefully will layer off, and wipe the
lotion good cleaning effect.
50ml/ Double tube, 12 double tube /carton.